OzFDM PC-ABS Sparkling 3D Printing Filament 1.75mm 1KG
Tax included. Shipping calculated at checkout
Product Features
- Exceptional Thermal Resistance
- Excellent Mechanical Properties
- High Impact Strength and Durability
- Excellent electrochemical properties of ABS
- Diameter: 1.75mm +/- 0.05mm
Choose options
Experience superior heat resistance with the Oz FDM PC-ABS 1.75mm ± 0.05 1KG filament. Featuring a heat deflection temperature of 123° Celsius, this PolyCarbonate-ABS Filament is an ideal choice for producing 3D-printed components that require exceptional heat resistance.
Product specifications:
Filament weight | 1KG |
Filament diameter | 1.75mm |
Dimensional tolerance | ±0.05mm |
Spool weight (empty) | 150g |
Spool weight (new) | 1.15KG |
Spool diameter outer | 200mm |
Spool diameter inner (hub) | 52mm |
Spool width | 65mm |
Package weight | 1.3KG |
Package dimensions | 210mm x 210mm x 75mm |
Print parameters:
Nozzle temperature | 250°C - 280°C (265°C recommended) |
Bed temperature | 90°C - 110°C (100°C recommended) |
Printing speed | 40mm/s - 60mm/s (50mm/s recommended) |
Support material | HIPS |
Physical Properties:
Density | ISO 1183 | 1.14~1.15 g/cm3 |
MFR(250°C/2.16Kg) | ISO 1133 | 19~22 g/10min |
Moisture Absorbtion(23°C/24h) | ISO 62 | <0.8 % |
Mechanical Properties:
Tensile Strength | ISO 527 | 43.5~45.5 Mpa |
Elongation at Break | ISO 527 | 24~26 % |
Flexural Modulus | ISO 527 | 800~950 Mpa |
Flexural Strength | ISO 178 | 71.5~74.5 Mpa |
Impact Strength | ISO 180 | 43.5~44.5 KJ/m² |
Thermodynamic Properties:
HDT @ 0.455 Mpa(66 psi) | ISO 75 | 123 °C |
Continuous Use Temperature | IEC 60216 | 130 °C |
Drying recommendation:
80°C for a minimum of 12 hours using a filament dryer / food dehydrator.
After printing we recommend annealing the finished model at 100°C for 1~3 hours to increase strength of the model.
Storage recommendation:
Airtight bag or container with desiccant in a cool, dark and dry area to prevent moisture absorption. For optimal long term storage we recommend drying the filament prior to sealing the filament spool in a vacuum bag with desiccant.