OzFDM High Speed PLA Filament
OzFDM PLA-HS is specially formulated with modified, toughened PLA to enable faster printing while maintaining strength, accuracy, and surface quality. Designed for use with most FDM printers, it offers reliable bed and layer adhesion, excellent dimensional stability and minimal warping or cracking throughout the printing process.
Its optimised flow properties let the filament melt and extrude evenly at higher printing speeds, which helps reduce production time while keeping clean details, smooth surfaces, and strong layer bonding. This makes PLA HS an excellent choice for rapid prototypes, detailed models, functional components and larger prints where both efficiency and dependable performance matter.
Easy to print and suitable for a wide range of applications, OzFDM PLA-HS delivers consistent results for beginners, hobbyists and professional users. Whether you are producing a single model or completing ongoing production work, it provides the speed, strength and reliability needed to bring your ideas to life with confidence.
26 Colours. Endless Possibilities.
26 versatile colours, offering everything from bold statement shades to soft pastels and practical neutrals. Each colour is produced for consistent extrusion, dependable colour and a smooth finish, allowing makers to print faster while achieving polished, professional results.
Ready for Multicolour Printing
OzFDM PLA HS is suitable for use with AMS systems, including Bambu Lab AMS and AMS Lite, provided the spool fits correctly and the filament is loaded according to the manufacturer’s instructions.
Its rigid and consistent structure supports reliable feeding, making it a great option for automated filament changes and multicolour printing.
For the best results, keep the filament dry and select an appropriate PLA or high speed PLA profile. Standard PLA is listed as supported by Bambu Lab AMS systems.
Getting to know High Speed PLA
Fast, Consistent Printing
OzFDM PLA-HS is engineered to support faster printing speeds while maintaining smooth and consistent extrusion.
Its optimised flow properties help produce clean details, even layers and dependable surface quality, allowing users to reduce printing time without sacrificing the overall appearance or accuracy of their finished parts.
Strong and Dimensionally Stable
Made using modified and toughened PLA, PLA-HS offers improved strength and durability compared with standard PLA.
Its excellent dimensional stability helps reduce warping, shrinking and deformation, making it suitable for detailed models, prototypes, functional components and larger prints that require accurate dimensions.
Reliable Adhesion and Easy Use
PLA-HS provides dependable bed adhesion and strong bonding between layers, helping minimise lifting, cracking and failed prints.
Its consistent performance and easy printing characteristics make it suitable for beginners, experienced makers and professional users seeking reliable results across a wide range of FDM printers.
High Speed PLA Technical Specifications
Product Specifications
Filament weight
1KG
Filament diameter
1.75mm
Dimensional tolerance
±0.03mm
Spool weight (empty)
150g
Spool weight (new)
1.15KG
Spool diameter outer
200mm
Spool diameter inner (hub)
52mm
Spool width
65mm
Package weight
1.3KG
Package dimensions
210mm x 210mm x 75mm
Drying recommendation:
40°C - 45°C for 4-6 hours using a filament dryer / food dehydrator.
Storage recommendation:
Airtight bag or container with desiccant in a cool, dark and dry area to prevent moisture absorption. For optimal long term storage we recommend drying the filament prior to sealing the filament spool in a vacuum bag with desiccant.
*Biodegradable under commercial composting conditions. Please do not throw into your compost bin at home.
Print Parameters
Nozzle temperature
190°C - 220°C
Bed temperature
25°C - 60°C
Printing speed
60mm/s - 350mm/s
Support material
PVA , PETG (as support interface)
Mechanical Properties
Tensile Strength (X-Y)
ISO 527
45~49 MPa
Tensile Strength (X-Z)
ISO 527
35~40 MPa
Elongation at Break (X-Y)
ISO 527
10.5~15.5 %
Elongation at Break (X-Z)
ISO 527
5~8 %
Tensile Modulus (X-Y)
ISO 527
2000~2100 MPa
Tensile Modulus (X-Z)
ISO 527
1950~2050 MPa
Flexural Strength (X-Y)
ISO 178
70~80 MPa
Impact Strength (X-Y)
ISO 180
4.5~5 kJ/m²
Physical Properties
Density
ISO 1183
1.25~1.26 g/cm³
MFR (190°C/2.16 kg)
ISO 1133
10~20 g/10min
Moisture Absorption (23°C/24h)
ISO 62
<0.3 %
Thermodynamic Properties
HDT @ 0.455 MPa (66 psi)
ISO 75
53 °C
Continuous Use Temperature
IEC 60216
50 °C