OzFDM PVA 3D Printing Support Filament 1.75mm 0.5KG
Tax included. Shipping calculated at checkout
Product Features
- Completely soluble in Water
- Diameter: 1.75mm +/- 0.05mm
- Ideal support material for PLA, TPU and PA
Choose options
OzFDM PVA is a 1.75mm print filament designed for use as a support material with PLA, TPU, and PA. Its water solubility ensures easy and clean post-processing of the 3D-printed object. With 0.5KG of filament, you can print several large projects with ease.
To work with the BambuLab AMS we recommend the following adapter :
https://www.printables.com/model/431541-bambu-lab-ams-small-spool-adapter
Product specifications:
| Filament weight | 0.5KG |
| Filament diameter | 1.75mm |
| Dimensional tolerance | ±0.05mm |
| Spool weight (empty) | 150g |
| Spool weight (new) | 0.65KG |
| Spool diameter outer | 180mm |
| Spool diameter inner (hub) | 55mm |
| Spool width | 49mm |
| Package weight | 0.8KG |
| Package dimensions | 210mm x 210mm x 75mm |
Print parameters:
| Nozzle temperature | 210°C - 230°C (220°C recommended) |
| Bed temperature | 25°C - 60°C (40°C recommended) |
| Printing speed | 40mm/s - 90mm/s (60mm/s recommended) |
| Support material | PVA |
Physical Properties:
| Density | ISO 1183 | 1.25~1.26 g/cm3 |
| MFR(250°C/2.16Kg) | ISO 1133 | 4~8 g/10min |
| Moisture Absorbtion(23°C/24h) | ISO 62 | 10~15 % |
| Saponification Degree | ISO 6293 | 74~76 % |
| Solubility (40μm flakes/20℃ water) | - | 97 s |
Mechanical Properties:
| Tensile Strength | ISO 527 | 65~75 Mpa |
| Elongation at Break | ISO 527 | 7~8.5 % |
| Flexural Modulus | ISO 527 | 1800~2100 Mpa |
| Flexural Strength | ISO 178 | 88~92.5 Mpa |
| Impact Strength | ISO 180 | 1.6~2.5 KJ/m² |
Thermodynamic Properties:
| HDT @ 0.455 Mpa(66 psi) | ISO 75 | 55 °C |
Drying recommendation:
50°C for a minimum of 3 hours using a filament dryer / food dehydrator.
Storage recommendation:
Airtight bag or container with desiccant in a cool, dark and dry area to prevent moisture absorption. For optimal long term storage we recommend drying the filament prior to sealing the filament spool in a vacuum bag with desiccant.