1.75 mm PLA Chameleon Dual Colour Filament - 1 KG

$34.95 AUD

Taxes included. Shipping calculated at checkout.

Chameleon

Dual Colour Chameleon Red-Orange

In stock

OzFDM PLA Chameleon Dual-Colour filament is made from high quality PLA material and features a dual-colour blend that creates a colour shifting effect throughout the print. The filament combines easy printability with a smooth surface finish, making it ideal for decorative parts, display models, and visually striking prints. The colour change effect varies depending on printing orientation and lighting, giving each print a unique appearance while maintaining the reliability and ease of use expected from PLA.

OzFDM’s PLA Chameleon Dual-Colour 1.75mm filament is a visually dynamic filament designed to create colour shifting prints with a smooth, high quality finish. Made from reliable PLA material, it combines easy printability with a dual-colour blend that produces a striking visual effect depending on print orientation and lighting. Ideal for decorative parts, display models, and creative projects, PLA Chameleon delivers consistent extrusion, strong layer adhesion, and a clean surface finish while offering a unique multi-tone appearance across each print.

Technical Data Sheet PDF

OzFDM PLA Chameleon Dual Colour spools in red-orange, yellow-green and blue-pink

Three OzFDM PLA Chameleon Dual Colour spools side by side

OzFDM's PLA Chameleon Dual-Colour Shade Range

Colour in Motion

PLA Chameleon Dual-Colour filament is available in a selection of vibrant colour combinations designed to create a shifting, multi-tone effect as your print catches the light. Each variant blends two colours into a single strand, producing a smooth transition across surfaces and adding depth and visual interest to finished prints.

The final appearance will vary depending on print orientation, layer height, and lighting, making every print uniquely its own.

Yellow-Green#5FAF4A
Blue-Pink#6B4FA3
Red-Orange#D24B2A

Screen colours are a guide only. The finished print varies with lighting, layer height and finish.

Smooth feeding and reliable performance in AMS systems

Designed for AMS Use

PLA Chameleon Dual-Colour filament is fully compatible with AMS systems and feeds reliably thanks to its consistent diameter and PLA base material.
It performs the same as standard PLA within multi-material setups, making it suitable for both single and multi-spool printing.
Keep the filament dry and feed it smoothly through the system to achieve optimal results, as with all decorative filaments.

Four OzFDM filament spools loaded in a Bambu Lab AMS unit

Performance Highlights

PLA Chameleon Dual-Colour Key Points

Dual-colour chameleon effect with smooth colour transitions
Easy to print PLA base material
AMS compatible for seamless multi-spool use
Excellent layer adhesion and surface finish
Ideal for decorative prints and display models
Reliable performance across a wide range of FDM printers

Technical Specifications

Product Specifications

Each spool of OzFDM’s PLA Chameleon Dual-Colour filament is vacuum sealed with a moisture absorbing desiccant so it is ready to print when you open the box.

Filament weight: 1 kg
Filament diameter: 1.75 mm
Dimensional tolerance: ±0.03mm
Spool weight (empty): 150 g
Spool weight (new): 1.15 kg
Spool diameter outer: 200 mm
Spool diameter inner (hub): 52 mm
Spool width: 65 mm
Package weight: 1.3 kg
Package dimensions: 210mm x 220mm x 75mm
Drying recommendation: 40°C – 45°C for 4–6 hours using a filament dryer / food dehydrator.
Storage recommendation: Airtight bag or container with desiccant in a cool, dark and dry area to prevent moisture absorption. For optimal long term storage we recommend drying the filament prior to sealing the filament spool in a vacuum bag with desiccant.

Print Parameters

Nozzle temperature: 190°C - 220°C
Bed temperature: 25°C - 60°C
Printing speed: 60mm/s - 90mm/s
Support material: PVA (as support interface)

Mechanical Properties

PLA Chameleon Dual-Colour is built on a standard PLA base, so strength is comparable to standard PLA and best suited to decorative prints and light functional parts.

Tensile strengthISO 527: 45~49 MPa
Elongation at breakISO 527: 13.5~15.5 %
Tensile modulusISO 527: 1000~1100 MPa
Flexural strengthISO 178: 69~75 MPa
Impact strengthISO 180: 4.5~5 kJ/m²